Pioneering Built-in Interfacial Electric Field for Enhanced Anion Exchange Membrane Water Electrolysis

Abstract

Here, we develop a nano-heterostructure composed of ultra-thin W5N4 shells over Ni3N nanoparticles (Ni3N@W5N4) as efficient catalysts, in which built-in interfacial electric field (BIEF) is created owing to the distinct lattice arrangements and work functions of biphasic metal nitrides. The BIEF facilitates the electron localization around the interface and enables high valence W and more exposed binding sites in the surface W5N4 shell for accelerating the water dissociation step, ultimately leading to a remarkable reduction in the energy barriers of RDS from 1.40 eV to 0.26 eV. Theoretical calculations and operando X-ray absorption spectroscopy analysis results demonstrated that surface W5N4 serves as the active species for HER. Moreover, the ultra-thin shell characteristics enable the optimized W5N4 with enhanced intrinsic catalytic activity to be fully exposed as active sites. Consequently, the Ni3N@W5N4 exhibits exceptional performance in alkaline HER (60 mV@10 mA cm-2) and remarkable long-term stability (500 mA cm-2 for 100 hours). When employed as the cathode in the AEMWE device, the synthesized Ni3N@W5N4 demonstrates stable performance for over 80 hours at a current density of 1 A cm-2.

Keywords: Anion exchange membrane; Built-in Interfacial Electric Field; Water electrolysis; non-precious metal catalysts.