Surface passivation has driven the rapid increase in the power conversion efficiency (PCE) of perovskite solar cells (PSCs). However, state-of-the-art surface passivation techniques rely on ammonium ligands that suffer deprotonation under light and thermal stress. We developed a library of amidinium ligands, of interest for their resonance effect-enhanced N-H bonds that may resist deprotonation, to increase the thermal stability of passivation layers on perovskite surfaces. This strategy resulted in a >10-fold reduction in the ligand deprotonation equilibrium constant and a twofold increase in the maintenance of photoluminescence quantum yield after aging at 85°C under illumination in air. Implementing this approach, we achieved a certified quasi-steady-state PCE of 26.3% for inverted PSCs; and we report retention of ≥90% PCE after 1100 hours of continuous 1-sun maximum power point operation at 85°C.