Carbon-based electrode materials have widely been used in supercapacitors. Unfortunately, the fabrication of the supercapacitors includes a polymeric binding material that leads to an undesirable addition of weight along with an increased charge transfer resistance. Herein, binder-free and lightweight electrodes were fabricated using powder processing of carbon nanofibers (CNFs) and graphene nanoplatelets (GNPs) resulting in a hybrid all-carbon composite material. The structural, morphological, and electrochemical properties of the composite electrodes were studied at different concentrations of GNPs. The specific capacitance (Cs) of the CNFs/GNPs composite was improved by increasing the concentration of GNPs. A maximum Cs of around 120 F g-1was achieved at 90 wt% GNPs which is around 5-fold higher in value than the pristine CNFs in 1 M potassium hydroxides (KOH), which then further increased to 189 F g-1in 6 M KOH electrolyte. The energy density of around 20 Wh kg-1with the corresponding power density of 340 W kg-1was achieved in the supercapacitor containing 90 wt% GNPs. The enhanced electrochemical performance of the composite is related to the presence of a synergistic effect and the CNFs establishing conductive/percolating networks. Such binder-free all-carbon electrodes can be a potential candidate for next-generation energy applications.
Keywords: binder-free; carbon nanofibers; energy storage; graphene nanoplatelets; nanocomposite; supercapacitor.
Creative Commons Attribution license.