Low-dimensional/three-dimensional perovskite heterojunctions have shown great potential for improving the performance of perovskite photovoltaics, but large organic cations in low-dimensional perovskites hinder charge transport and cause carrier mobility anisotropy at the heterojunction interface. Here, we report a low-dimensional/three-dimensional perovskite heterojunction that introduces strong aromatic conjugated low-dimensional perovskites in p-i-n devices to reduce the electron transport resistance crossing the perovskite/electron extraction interface. The strong aromatic conjugated π-conjugated network results in continuous energy orbits among [Pb2I6]2- frameworks, thereby effectively suppressing interfacial non-radiative recombination and boosting carrier extraction. Consequently, the devices achieved an improved efficiency to 25.66% (certified 25.20%), and maintained over 95% of the initial efficiency after 1200 hours and 1000 hours under ISOS-L-1I and ISOS-D-1 protocols, respectively. The chemical design of strong aromatic conjugated molecules in perovskite heterojunctions provides a promising avenue for developing efficient and stable perovskite photovoltaics.
© 2024. The Author(s).