Micro Tensile bond strength and microleakage assessment of total-etch and self-etch adhesive bonded to carious affected dentin disinfected with Chlorhexidine, Curcumin, and Malachite green

Abstract

Aims and objectives: Assessment of micro tensile bond strength (microTBS) and micro-leakage scores of total-etch adhesive (TAE) and self-etch adhesive (SAE) bonded to carious affected dentin (CAD) sterilized using different cavity disinfectant (curcumin photosensitizer (CP) and malachite green (MG) and Chlorhexidine (CHX) in comparison to no disinfection (ND) control group.

Materials and methods: One hundred and twenty human molars having International Caries Detection and Assessment System (ICDAS) scores of 4 and 5 were included. Visual inspection, dental explorer hardness testing, and caries detector solution using 5% basic Fuchsin dye solution was applied to dentin to identify the CAD surface. All the specimens were divided into four groups (n = 30) according to the cavity disinfectants used. Group A: 2% CHX, Group B: CP, Group C: MG, and Group D: ND. Each group was further divided into two subgroups (n = 15) based on the adhesion protocol. Groups A1, B1, C1, and D1 were held using TEA, and groups A2, B2, C2, and D2 were adhered using SEA system. The composite material was then built in 2 mm increments and then cured with light. MicroTBS and failure mode assessment using a universal testing machine (UTM) and stereomicroscope at a 40X magnification was performed on 10 samples from each subgroup. The microleakage assessment was performed using a dye penetration test on five samples from each group. ANOVA and Tukey post-hoc tests were used to compare means and standard deviation (SD) of bond strength and microleakage (p < 0.05). RESULTS The maximum microTBS was displayed by A1= CHX and TEA (13.28± 1.01 MPa). The lowest bond scores were demonstrated by C2= MG and SEA (5.98±0.44 MPa). The highest micro-leakage was exhibited by C1= MG and TEA (58.32 ± 2.11 nm). Whereas, the lowest micro-leakage values were displayed by A2= CHX and SEA (24.34± 1.11 nm).

Conclusion: Chlorohexidiene displayed better bond strength and the lowest microleakage scores with Total-etch adhesive and Self-etch adhesives when used as a cavity disinfectant. Total-etch adhesives performed better in terms of microTBS scores whereas self-etch adhesives displayed superior seal ability within the same disinfectant group.

Keywords: Carious affected dentin; Chlorhexidine; Malachite green; Photodynamic Therapy; Self-etch adhesive; Total etch adhesive.