Sumatran elephants (Elephas maximus sumatranus) are the world's largest living land mammals. The elephant's digestive system can only absorb 40% of the nutrients in digested feed, and the remainder is excreted as dung. Elephant dung waste can be used as a particleboard material due to its high fiber content. The objectives of this study are: (i) to prepare elephant dung waste as raw material for particleboard, (ii) to improve elephant dung particleboard's physical and mechanical properties using wood shavings, and (iii) to study the influence of several parameters on the physical and mechanical properties of particleboard. The particleboard dimensions and density were set at 20 cm × 20 cm × 1 cm and 0.8 g/cm3, respectively. The mixture ratio of elephant dung and wood shavings was 100/0, 90/10, 80/20, 70/30, 60/40, and 50/50 (% w/w). This mixture ratio of particles was sprayed with 7% isocyanate adhesive. The pressing at a pressure of 30 kg/cm2 for 5 min and 160 °C was used in this study. The physical and mechanical properties of particleboard were tested according to JIS A 5908 (2003) standard. The result shows that the addition of wood shaving improved the elephant dung particleboard's physical and mechanical properties. Except for moisture content and water absorption, the addition of wood shavings has a significant effect on elephant dung particleboard's physical and mechanical properties. The best ratio of elephant dung and wood-shaving for this research is 50/50 and has fulfilled the JIS A 5908-2003 standard, except for thickness swelling.
Keywords: elephant dung fibers; isocyanate; particleboard; wood shavings.