Electrospinning of small diameter vascular grafts with preferential fiber directions and comparison of their mechanical behavior with native rat aortas

Abstract

Conventional electrospun small diameter vascular grafts have a random fiber orientation. In order to achieve mechanical characteristics similar to a native blood vessel, a controllable fiber orientation is of interest. In this study the electrospinning jet was directly controlled by means of an auxiliary, changeable electrostatic field, so that the fibers could be deposited in adjustable orientations. Prostheses with circumferentially, axially, fenestrated and randomly aligned fibers were electrospun on Ø2mm mandrels out of a thermoplastic polyurethane (PUR) and a polylactid acid (PLLA). The impact of the materials and the various preferential fiber orientations on the resulting biomechanics was investigated and compared with that of the native rat aorta in quasistatic and dynamic hoop tensile tests. The test protocol included 3000 dynamic loading cycles in the physiological blood pressure range and ended with a quasistatic tensile test. Any orientation of the fibers in a particular direction resulted in a significant reduction in scaffold porosity for both materials. The standard randomly oriented PUR grafts showed the highest compliance of 29.7 ± 5.5 [%/100 mmHg] and were thus closest to the compliance of the rat aortas, which was 37.2 ± 6.5 [%/100 mmHg]. The maximum tensile force was increased at least 6 times compared to randomly spun grafts by orienting the fibers in the circumferential direction. During the 3000 loading cycles, creeping of the native rat aorta was below 1% whereas the electrospun grafts showed creeping up to 2.4 ± 1.2%. Although the preferred fiber orientations were only partially visible in the scanning electron micrographs, the mechanical effects were evident. The investigations suggest a multi-layer wall structure of the vascular prosthesis, since none of the preferred fiber directions and the materials used could imitate the typical j-shaped mechanical characteristics of the rat aorta.

Keywords: Dynamic measurement; Electrospinning; Fiber orientation; Mechanical characterization; Small diameter blood vessel; Vascular graft.