Major strides have been made in the development of materials and devices based around low-dimensional hybrid group 14 metal halide perovskites. Thus far, this work has mostly focused on compounds containing highly toxic Pb, with the analogous less toxic Sn materials being comparatively poorly evolved. In response, the study herein aims to (i) provide insight into the impact of templating cations upon the structure of n = 1 2D tin iodide perovskites (where n refers to the number of contiguous two-dimensional (2D) inorganic layers, i.e., not separated by organic cations) and (ii) examine their potential as light absorbers for photovoltaic (PV) cells. It was discovered through systematic tuning of organic dications that imidazolium rings are able to induce the formation of (110)-oriented materials, including examples of "3 × 3" corrugated Sn-I perovskites. This structural outcome is a consequence of a combination of supramolecular interactions of the two endocyclic N atoms of the imidazolium rings with the Sn-I framework, and the comparatively high tendency of Sn2+ ions to stereochemically express their 5s2 lone pairs . More importantly, the resulting materials feature very short separations between their 2D inorganic layers with iodide-iodide (I···I) contacts as small as 4.174 Å, which is among the shortest ever recorded for 2D tin iodide perovskites. These proximate inorganic distances, combined with the polarizable nature of the imidazolium moiety, eases the separation of photogenerated charge within the materials. This is evident from the measurement of excitonic activation energies as low as 83(10) meV for ImEA[SnI4]. When combined with superior light absorption capabilities relative to their lead congeners, this allowed the fabrication of lead-free solar cells with incident photon-to-current and power conversion efficiencies of up to 70% and 2.26%, respectively, which are among the highest values reported for pure n = 1 2D group 14 metal halide perovskites. In fact, these values are superior to the corresponding lead iodide material, which demonstrates that 2D Sn-based materials have significant potential as less toxic alternatives to their Pb counterparts.
Keywords: 2D perovskites; crystal engineering; iodostannates; lead-free; lone pair steric activity; solar cells.